This study investigates the machinability of Continuous Fiber-Reinforced Thermoplastic Composite (CFRTP) produced via Material Extrusion (MEX) additive manufacturing, focusing on drilling as a critical post-processing step in hybrid manufacturing. CFRTP components, fabricated from 3K carbon fibers and a PLA matrix, were subjected to systematic drilling tests under varying cutting speeds (50–110 m/min) and feed rates (0.06–0.24 mm/rev). Thrust force (Fz) and torque (Mz) were recorded using a high-precision dynamometer to evaluate the influence of cutting parameters on mechanical loads and damage mechanisms. Results indicate that increasing the feed rate significantly increases Fz and Mz, promoting fiber pull-out, delamination, and edge deformation, particularly at hole entry and exit regions.