ABSTRACT Polyimide (PI) is widely utilized in high-power electronic devices due to its outstanding thermal
stability, superior mechanical strength, excellent electrical insulation, and chemical resistance. However,
its intrinsically low thermal conductivity hinders its application in highly integrated systems. To address
this limitation, the present study successfully prepared KH550-functionalized Boron Nitride Nanosheets
(BNNs@KH550)/Polyimide composite films through a combined method of ball milling and silane coupling
agent KH550 surface modification, aiming to develop advanced film materials that meet the stringent
requirements of high-power electronics. XPS analysis confirmed the successful grafting of KH550 onto
the BNNs surface, which significantly improved the dispersion uniformity of BNNs within the PI matrix
and effectively suppressed agglomeration. In terms of performance, the KH550 modification demonstrated
positive effects: contrasting with the continuous decline in breakdown strength caused by unmodified BNNs,
the BNNs@KH550/PI film exhibited a slight enhancement in breakdown strength, reaching 543.3 kV/mm at
a low filler loading of 2 wt%, and maintained the dielectric dissipation factor at an extremely low level, nearly
identical to that of pure PI.
Study on the Thermal Conductivity and Insulation Properties of Polyimide Composite Films Filled With Surface-Coated BNNs